机译:五年后使用不同粘合策略在五年模拟牙线压力下产生的粘合剂牙本质界面的降解
Univ Fed Ceara Postgrad Program Dent Dept Restorat Dent Fortaleza Ceara Brazil;
CEU Carden Herrera Univ Dept Odontol Fac Ciencias Salud Valencia Spain;
Univ Fed Ceara Postgrad Program Dent Dept Restorat Dent Fortaleza Ceara Brazil;
Univ Fed Ceara Postgrad Program Dent Dept Restorat Dent Fortaleza Ceara Brazil;
Univ Estadual Campinas Piracicaba Dent Sch Piracicaba Brazil;
Univ Leuven Dept Oral Hlth Sci KU Leuven BIOMAT Leuven Belgium;
Univ Estadual Campinas Piracicaba Dent Sch Piracicaba Brazil;
Univ Estadual Campinas Piracicaba Dent Sch Piracicaba Brazil;
Okayama Univ Hosp Ctr Innovat Clin Med Okayama Japan;
aging; dentin; bond strength; electron microscopy; pulpal pressure;
机译:五年后使用不同粘合策略在五年模拟牙线压力下产生的粘合剂牙本质界面的降解
机译:在模拟牙髓压力下储存一年的水期间,牙本质键降解的进展缓慢。
机译:模拟的纸浆压力,直接和间接水老化引起的树脂-牙本质界面的水解降解
机译:由于接口处产生的缺陷,导致功率RF N-LDMOS器件的导通电阻降低
机译:由于颗粒飞灰的沉积,整体气化联合循环(IGCC)模拟的薄膜冷却涡轮叶片压力表面上的隔热涂层性能下降
机译:模拟牙髓压力下聚维酮碘对牙本质微拉伸粘合强度的影响
机译:长期模拟牙髓对不同粘合策略的树脂留剂粘接强度和纳米盖的影响