Modification of Bismaleimide Resin by Poly(ethylene phthalate-co-ethylene terephthalate), Poly(ethylene phthalate-co-ethylene4,4'-biphenyl dicarboxylate), and Poly(ethylene phthalate-co-ethylene 2,6-naphthalene dicarboxylate)

摘要

Aromatic polyesters were prepared and used to improve the brittleness of bismaleimide resin, composed of 4,4 min-bismaleimidodiphenyl methane and o,o min -diallyl bisphenol A (Martrimid 5292 A/B resin). The aromatic polyesters included PEPT [poly (ethylene phthalate-co-ethylene terephthalate)], with 50 mol % of terephthalate, PEPB [poly9ethylene phthalate-co-ethylene 4,4 min-biphenyldicarboxylate]], with 50 mol % of 4,4 min -biphenyl dicarboxylate, and PEPN [poly(ehhylene phthalate-co-ethylene2,6-naph-thalena dicarboxylate0), with 50 mol %2,6-naphthalene dicarboxylate unit. The polyesters were effective modifiers for improving the brittleness of the bismaleimide resin. For example, inclusion of 15 wt % PEPT (MW = 9300) led to a 75% increase in fracture toughness,with retention in flexural properties and a slight loss of the glass-transition temperature, compared with the mechanical and thermal properties of the unmodified cured bismaleimide resin. Microstructures of the modified resins were examined by scanning electron microscopy and dynamic viscoelastic analysis. The toughening mechanism was assessed as it related to the morphological and dynamic viscoelastic behaviors of the modified bismaleimide resin system.