NEW GENERATION OF CHITOSAN-(ACRYLIC ACID)-MAGNETITE NANOSPHERES:SYNTHESIS, CHARACTERIZATION AND CELL VIABILITY TEST IN VITRO

机译:新一代壳聚糖 - (丙烯酸)-MAGNETATE纳米球:体外合成,表征和细胞活力试验

获取原文

摘要

A facile approach to a new generation of chitosan-(acrylic acid)-magnetite nanospheres (CS-AA-Fe3O4) was demonstrated. TEM morphology indicated that magnetite nanoparticles (diameter about 20 nm) were embedded in CS-AA-Fe3O4 nanospheres (130 nm). Significant swelling of CS-AA-Fe3O4 was expressed and the hydrodynamic size of CS-AA-Fe3O4 was 330 nm. The CS-AA-Fe3O4 was non-toxic and tended to migrate into MG-63 cells via endocytosis. It has potential applications as drug delivery system.
机译:对新一代的壳聚糖(丙烯酸)-MAGNETATE纳米球(CS-AA-FE3O4)进行了一种容易的方法。 TEM形态表明,磁铁矿纳米颗粒(直径约20nm)嵌入CS-AA-Fe 3 O 4纳米球(130nm)中。表达CS-AA-Fe3O4的显着溶胀,CS-AA-Fe3O4的流体动力学尺寸为330nm。 CS-AA-Fe3O4无毒,倾向于通过内吞作用迁移到Mg-63细胞中。它具有潜在的应用作为药物输送系统。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号