Growth and Characterization of Ammonium Dihydrogen Phosphate (ADP) doped with H_3BO_3 Crystals Grown by Slow Evaporation Method

摘要

Ammonium dihydrogen phosphate (ADP) crystals is very interesting due to its nonlinear optical property. This study investigated on improving of material for academic use by adding boric acid to modify ADP crystals. Slow evaporation method in aqueous solutions of pure ADP and ADP doped with three concentrations of H3BO3 as 0.1, 1.0, 5.0 %wt were studied. The grown crystals were confirmed tetragonal structure by powder X-ray diffraction studies. The FTIR spectrum analysis presented various functional groups of boron in three conditions of doped ADP. TGA study was comfirned the temperature stability at 220 °C for both pure and doped ADP crytals. The machanical stress was analyzed by Vicker's hardness measurement. The results of this analysis showed boric acid doped 1.0 %wt had superior machanical stress from 10 to 75 grams. ADP doped with boric acid at 1.0 %wt was accepted in all test properties.