SIALON-CONTAINING ALUMINA-CHROME COMPOSITE REFRACTORY AND ITS PRODUCTION
SIALON-CONTAINING ALUMINA-CHROME COMPOSITE REFRACTORY AND ITS PRODUCTION
展开▼
机译:含赛隆的铝铬复合耐火材料及其生产
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To improve thermal shock, corrosion and wear resistances by firing a mixture of alumina, magnesia, spinel or zirconia with a powdery chromium oxide-aluminum mixture and a powdery silicon nitride-aluminum nitride mixture in an atmosphere of nitrogen. ;SOLUTION: A compsn. is prepd. by blending 10-50wt.% one or more kinds of aggregates selected from among alumina, magnesia, spinel and zirconia each having 0.3-1mm particle diameter with 25-60wt.% powdery chrominum oxide-aluminum mixture having a molar ratio of 1:2 and 20-40wt.% powdery silicon nitride-aluminum nitride mixture having a ratio of 1:(0.5-1). The compsn. is fired at ≥1,400°C in an atmosphere of nitrogen under atmospheric pressure optionally after press compacting at ≥600°C under ≥10MPa pressure to obtain the objective sialon-contg. alumina-chrome composite refractories having ≤5% porosity and contg. alumina, magnesia, spinel or zirconia uniformly dispersed in the sialon-alumina-chrome matrix.;COPYRIGHT: (C)1998,JPO
展开▼