METHOD FOR PRODUCING RESIN SOLUTION COMPOSITIONS FOR CR-FREE ANTI-FINGERPRINT PROPERTY HAVING HIGH CORROSION RESISTANCE WITH EXCELLENT CHEMICAL RESISTANCE AND CONDUCTIVITY, AND CR-FREE GALVANIZED STEEL SHEET COATED THEREOF
METHOD FOR PRODUCING RESIN SOLUTION COMPOSITIONS FOR CR-FREE ANTI-FINGERPRINT PROPERTY HAVING HIGH CORROSION RESISTANCE WITH EXCELLENT CHEMICAL RESISTANCE AND CONDUCTIVITY, AND CR-FREE GALVANIZED STEEL SHEET COATED THEREOF
The present invention omit the traditional chromate and phosphate coating on galvanized steel surfaces and also from 0.9 to 1.3 g / m 2 of chemical resistance and corrosion resistance while having a property of high electrical conductivity , as additional surface -fingerprint product for the general anti-fingerprint coating resin after conventional phosphate and chromate treatment by coating a polymeric resin relates to a chromium -free (Cr-free) anti-fingerprint coating resin liquid steel production to secure , its purpose is electroplated zinc demand is not growing in recent years , and that environmentally friendly consumer electronics market providing a surface treated steel containing chromium the chromium -free galvanized steel with resin solution and this method for plating steel surface treatment with a base .
展开▼
机译:本发明省去了镀锌钢表面上的传统铬酸盐和磷酸盐涂层,另外还具有0.9至1.3 g / m 2 Sup>的耐化学性和耐腐蚀性,同时具有高导电性,作为附加表面-常规防指纹涂料树脂经过常规磷酸盐和铬酸盐处理后,通过涂覆聚合物树脂制成的指纹产品,涉及到无铬(Cr-free)防指纹涂料树脂液态钢的生产安全,其目的是电镀锌需求量大。近年来增长不大,环保的消费电子市场提供了一种含铬的表面处理的钢和一种无铬的镀锌树脂溶液,以及用碱对钢板进行表面处理的这种方法。
展开▼