Method for producing powder forsterite powder, forsterite powder, sintered forsterite, insulating ceramic composition, and multilayer ceramic electronic component

摘要

A forsterite powder with superior characteristics which can be sintered at a relatively low temperature can be economically produced, when a magnesium source, a silicon source, and copper particles are mixed to prepare a mixed powder containing 300 to 2,000 ppm by weight of the copper particles, and the mixed powder is fired. The magnesium source used is preferably Mg(OH)₂, and the silicon source used is preferably SiO₂. A polycrystalline forsterite powder is preferably produced. The magnesium source, the silicon source, and the copper particles can be mixed in the presence of a solvent to prepare the mixed powder. The forsterite powder preferably contains 300 to 2,000 ppm by weight of copper, has a particle size of 0.20 to 0.40 μm and has a crystal size of 0.034 to 0.040 μm.