Process for identification of molybdenum structure
展开▼
机译:钼结构鉴定方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention relates to the field of metallurgy and can be used for identification of metal structure.The process for identification of molybdenum structure involves anodic treatment of molybdenum with subsequent examination of the treated surface using an optical device, and identification of structure is carried out for 10…120 seconds with an interelectrode gap of 0.1…0.3 mm in a flow electrolyte based on NaOH (KOH) at a concentration of 50…200 g/L, a current density of 10…30 A/dm2 at room temperature.