Structural and superconducting features of Tl-1223 prepared at ambient pressure

摘要

This study provides an account of the bulk preparation of TlBa2Ca2Cu3O9-delta (Tl-1223) superconductor at ambient pressure, and the critical temperature (T-c) features under thermal-annealing conditions. The 'as-prepared' Tl-1223 (T-c = 106 K) presents a significantly higher T-c = 125 K after annealing the polycrystalline material in either flowing Ar + 4% H-2, or N-2 gases. In order to understand the fundamental reasons for a particular Tc, we refined the average bulk structures using powder x-ray diffraction data. Although Ar. +. 4% H2 annealed Tl-1223 shows an increased 'c' lattice parameter, it shrinks by 0.03% (approximately unchanged) upon N2 anneal. Due to such indeterminate conclusions on the average structural changes, local structures were investigated at using aberration-corrected scanning-transmission electron microscopy technique. Similar compositional changes in the atomic arrangements of both annealed-samples of Tl-1223 were detected in which the plane containing a Ca atomic layer gives a non-uniform contrast, due to substitution of some heavier Tl. In this report, extensive bulk properties are summarized through temperature-dependent resistivity, and shielding and Meissner fractions of magnetic susceptibility results; the bulk and local structures are investigated to correlate to properties.