Transverse cracking prevention and segregation reduction in slab continuous casting

Dmitry Sediako; Kuan-Ju Lin

首页> 外文期刊>Steelmaking Conference Proceedings >Transverse cracking prevention and segregation reduction in slab continuous casting

【24h】

Transverse cracking prevention and segregation reduction in slab continuous casting

机译：板坯连铸的横向裂纹预防和减少偏析

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

Quality of continuous cast steel has been improved bycarrying out an integrated analysis of steel casting and slab formation.Operational parameters of steel casting on the #1 slab continuouscasting machine (SCC) at China steel corporation have been analyzedin this study.

机译：通过对铸钢和板坯的形成进行综合分析，提高了连铸钢的质量。本研究分析了中国钢铁公司＃1板坯连铸机上的铸钢操作参数。

著录项

来源
《Steelmaking Conference Proceedings》 |1997年第0期|共7页
作者
Dmitry Sediako; Kuan-Ju Lin;
展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类炼钢;
关键词
极坯连铸; 横裂纹; 减少; 偏析;

机译：极坯连铸;横裂纹;减少;偏析;

相似文献

外文文献
中文文献
专利

1. Transverse cracking prevention and segregation reduction in slab continuous casting [J] . Dmitry Sediako, Kuan-Ju Lin Steelmaking Conference Proceedings . 1997,第0期

机译：板坯连铸的横向裂纹预防和减少偏析
2. Effect of cooling rate on the hot ductility of boron bearing steel during continuous casting (Study for prevention of corner crack on continuous casting slab) [J] . Kyungchul Cho, Yangmo Koo, Joongkil Park Journal of Korean Institute of Metal and Materials . 2008,第6期

机译：冷却速度对连铸过程中含硼钢热延展性的影响（防止连铸板角裂的研究）
3. Methods for Assessment of Slab Centre Segregation as a Tool to Control Slab Continuous Casting with Soft Reduction [J] . Hubert PREGLINGER, Sergiu ILIE, Peter REISINGER ISIJ international . 2006,第12期

机译：板坯中心偏析的评估方法作为通过软压下控制板坯连铸的工具
4. Transverse Cracking Prevention and Segregation Reduction in Slab Continuous Casting [C] . Dmitry Sediako, Kuan-Ju Lin, Shih-Yung Lee, Steelmaking conference . 1997

机译：板坯连铸的横向裂纹预防和减少偏析
5. A model and data-based analysis of longitudinal surface cracking in the continuous casting of middle carbon steel slabs. [D] . Suni, Jaakko Paavo. 1991

机译：中碳钢板坯连铸纵向表面开裂的模型和基于数据的分析。
6. Cracking and segregation in high-alloy steel 0.4C1.5Mn2Cr0.35Mo1.5Ni produced by thick continuous casting [O] . Rensheng Chu, Zhanjun Li, Yong Fan, 2019

机译：厚连铸0.4C1.5Mn2Cr0.35Mo1.5Ni高合金钢的裂纹和偏析
7. Finite element study of the effect of some local defects on the risk of transverse cracking in continuous casting of steel slabs [O] . Pascon, Frédéric, Habraken, Anne 2007

机译：钢板局部连铸局部缺陷对横向裂纹风险影响的有限元研究
8. Criteria for the Formation of Cracks during Continuous Casting of Special Steels. Cost 504 Casting Technology Project SF 3. Final Report 1988-91. [R] . Holappa, L., Louhenkilpi, S., Miettinen, J. 1991

机译：特种钢连铸过程中裂纹形成的标准。成本504铸造技术项目sF 3.最终报告1988-91。

Transverse cracking prevention and segregation reduction in slab continuous casting

摘要

著录项

相似文献

相关主题

期刊订阅