Porosity of micro-mesoporous zeolites prepared via pseudomorphic transformation of zeolite Y crystals: A combined isothermal sorption and thermodesorption investigation

摘要

The porosity of micro-mesoporous zeolite crystals was studied by sorption measurements with different probe molecules. Recrystallization of a commercial zeolite Y with addition of a cationic surfactant as the mesostructure directing agent was used as a 'constructive' synthesis route to generate mesoporosity inside the zeolite crystals. The obtained material was characterized by X-ray powder diffraction, scanning and transmission electron microscopy and thermogravimetric analysis. The adsorption-desorption isotherms of N2 and Ar at 77 K and quasi-equilibrated temperature programmed desorption and adsorption (QE-TPDA) of n-hexane and n-nonane were performed in order to characterize the hierarchical porous network. The QE-TPDA of n-hexane on the recrystallized zeolite confirmed the faujasite type structure and showed some distortion of the micropores. The pore size distributions calculated from the QE-TPD of n-nonane are more precise than those determined from nitrogen desorption isotherms, since determined from numerous experimental data points recorded in one desorption cycle.