Studies on the utilization of Hura crepitans L. seed oil in the preparation of alkyd resins.

摘要

The utilization of Hura crepitans seed oil in the formulation of alkyd resins was investigated using a two-stage alcoholysis-polyesterification method. The percentage yield of the oil was 36.4%; and the physicochemical characterization revealed that the seed oil is an unsaturated semi-drying oil. The fatty acid profile of the oil showed that it contains linoleic acid (81.6%) as the most abundant fatty acid, and two other fatty acids: palmitic acid (16.92%) and stearic acid (1.76%). Short (I), medium (II) and long (III) oil alkyds were synthesized using the oil, glycerol and phthalic anhydride in different ratios. Properties of the three prepared samples of H. crepitans seed oil alkyds having oil content of 30% (I), 50% (II), and 65% (III) were evaluated. The alkyd resins synthesized compared favourably with the commercially available alkyd resin. The presence of unsaturation in the oil was confirmed by infra-red peak at 2930 cm-1 attributed to C=C stretch. The infra-red peaks of the sample also compared well with that of the commercial sample indicating that H. crepitans seed oil has been successfully converted to alkyd resin. Evaluation of prepared alkyds by determination of acid values, solubility in butanol and toluene, resistance of dry film to acid, alkali and water, and drying time revealed that H. crepitans seed oil is a potential raw material for the coating industry.