Assembly of surface-defect single-crystalline strontium titanate nanocubes acting as molecular bricks onto surface-defect single-crystalline titanium dioxide (B) nanorods for efficient visible-light-driven photocatalytic performance

摘要

Ti3+ self-doped single-crystalline SrTiO3-x nanocubes acting as molecular bricks are successfully assembled onto Ti3+ self-doping single-crystalline TiO2-x(B) nanorods through an effortless two-step hydrothermal process coupled with an in situ solid-state chemical reduction method. SrTiO(3-x )nanocubes act as molecular bricks, which are uniformly assembled onto the surface of TiO2-x(B) nanorods due to lattice matching. The band gap of the resultant SrTiO3-x/TiO2-x(B) sample is similar to 2.97 eV, which exhibits excellent photocatalytic performance for the reduction of Cr(VI) and hydrogen production under visible light. The apparent rate constant k value for the photocatalytic reaction of SrTiO3-x/TiO2-x(B) for Cr(VI) reduction is similar to 8 times higher than that of white TiO2(B). The photocatalytic hydrogen production rate for SrTiO3-x/TiO2-x(B) is similar to 160.2 mu mol g(-1) h(-1), which is similar to 5 times higher than that of white TiO2(B). The enhanced photocatalytic activity can be considered to be caused by a synergetic effect of heterojunction formation and the introduction of Ti3+ self-doping, which can not only facilitate the separation of photogenerated charge carriers between TiO2-x(B) and SrTiO3-x, but also broaden the photoresponse from the UV to visible-light region. (C) 2018 Elsevier Inc. All rights reserved.