Mechanical, Chemical, Thermal, and Rheological Properties of Recycled PA6/ABS Binary and PA6/PA66/ABS Ternary Blends

摘要

The effects of multiple injection molding cycles on the chemical and mechanical properties of PA6/ABS and PA6/PA66/ ABS blends are investigated. The chemical structures of both PA6/ABS binary and PA6/PA66/ABS ternary blends do not alter after recycling process. For PA6/ABS binary blend, it is found that the tensile strength, strain at break, elastic modulus, impact strength, flexural strength, and modulus of recycled blend decrease by 6.49%, 15.19%, 21.00%, 9.41%, 7.09%, and 8.25%, respectively, while MFI increases by 23.59% as compared with the virgin blend. After five recycling process for PA6/PA66/ABS ternary blend, the tensile strength, strain at break, and impact strength of recycled blend decrease by 18.00%, 50.80%, and 87.27%, respectively. However, flexural strength and modulus of PA6/PA66/ABS blend increase slightly. For virgin PA6/PA66/ABS blend, MFI value was 7.7 g/10 min and with recycling this value showed an important increase to 31.56 g/10 min after five cycles.