Structural and Magnetic Phase Transitions in ErFe_2H_x Hydrides

摘要

Temperature dependences of the lattice parameters, magnetization and magneticsusceptibility have been measured for the ErFe_2H_x hydrides with different hydrogen contentxandfor the ErFe_2D_(3,t)deuteride. For the samples with a hydrogen content of about 3.1, structuraltransition from the cubic to the rhombohedral phase has been observed in the temperature range 280— 310 K. Small variation of hydrogen content does not shift the transition temperature, butinfluences the amount of the low-temperature rhombohedral phase. The temperature dependence ofmagnetization shows up an anomaly in the range of the phase transition, which is due to thedifference in the magnitudes of magnetic moments and exchange interactions in two phases.Structural and magnetic studies point to a diffusion nature of the phase transition. Upon heating thesamples in vacuum there takes place decomposition of the hydride. The hydride with x 1.6 whichforms at the intermediate stage of decomposition possesses an ordering temperature higher than thatfor the parent ErFe_