Enhanced Mechanical and Thermal Properties of Polyimide/Organically Modified Montmorillonite Hybrid Film Based on Stable Poly(amic acid) Ammonium Salt

摘要

In this study, polyimide/organlcally modified montmorillonite (PI/OMMT) hybrid film was prepared by in situ polymerization from the stable poly(amic acid) ammonium salt/OMMT (PAAS/OMMT) precursor hybrid. PAAS was obtained by incorporating calculated triethylamine into terpolymer poly(amic acid) (PAA), which was synthesized by pyromellitic dianhydride (PMDA), 4,4'-oxydianiline and p-phenylenediamine in dimethylaceta-mide (DMAc). OMMT as a type of layered clays was prepared through surface treatment of montmorillonite (MMT) with 1-hexadecylamine. Mechanical property measurements of PI/OMMT hybrid film indicated that the addition of 5 wt% of OMMT increased the Young's modulus of PI film up to 11.24 GPa, which is 58% higher than the pristine PI film from PAAS. Besides, the tensile strength Increased to 168.36 MPa, which was higher than that of PI film derived from PAA (164.3 MPa) and PI film derived from PAAS (145.2 MPa). Moreover, the thermal stabilities of PI/OMMT hybrid film with appropriate OMMT content were also better than those of original PI films.