Synthesis of Mullite by Means of Transferred and Nontransferred Arc Plasma Melting

摘要

Arc plasma melting technique is a simple method for the synthesis of high melting point materials. In this article, mullite was synthesized by transferred arc plasma (TAP) and nontransferred arc plasma (non-TAP) melting processes, and the results were compared. The mixes of alumina and silica powders (3:2 mole ratios) were ball milled for four hours and then melted in an arc plasma torch, used in transferred and nontransferred mode, at 5Â kW input power and two minutes of processing time. Argon gas was used as a plasma-forming gas. The crystalline phases and the microstructural features of the melted samples were determined by X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. A complete crystallization of mullite, with dense, thick whiskers-shaped crystals, was achieved in TAP processing of the alumina/silica system. On the other hand, the non-TAP process produced porous mullite along with a small amount of residual alumina phase. Differential thermal analysis (DTA) curves of the synthesized mullite samples allowed a deeper understanding of the mechanisms of mullite formation during the two different processes.View full textDownload full textKeywordsArc plasma, Microstructure, Mullite, Nontransferred arc, Transferred arc, X-ray techniquesRelated var addthis_config = { ui_cobrand: "Taylor & Francis Online", services_compact: "citeulike,netvibes,twitter,technorati,delicious,linkedin,facebook,stumbleupon,digg,google,more", pubid: "ra-4dff56cd6bb1830b" }; Add to shortlist Link Permalink http://dx.doi.org/10.1080/10426910903536725