Aiming at the die wear problem of ultra high strength steel stamping forming,an effective and fast method was proposed for predicting die wear and working life.The method adopted Archard wear theory in order to obtain mould wear data after stamping forming.Die wear was mainly concentrated in the die round corners.The factors affecting die wear were analyzed systematically.These factors include die hardness,stamping speed and die material.The results showed that the die wear decreased effectively when the die hardness reached 60 ~ 65 HRC.The die wear was positively correlated with the stamping speed.Wear cumulation method was used to predict the service life of die,which had stamped 7500 times. the difference between die wear calculated by simulation and test data was only 1.47%,which showed that the method was feasible.The method has an important practical value in determining reasonable stamping process and designing die structure.%针对超高强钢板冲压模具的磨损问题，提出一种有效而快捷的预测模具磨损量和使用寿命的方法.该方法采用 Archard 磨损理论，得到冲压成型结束后模具的磨损区域主要集中在模具圆角处.系统地研究了模具硬度、冲压速度和模具材料对模具磨损程度的影响.结果表明：模具硬度达到60~65 HRC 时能有效减小磨损量；模具磨损量与冲压速度成正相关关系.采用磨损累积法预测模具修模前的使用寿命，模拟得到的冲压7500次的模具磨损量与试验数据仅相差1.47%，表明该方法是正确可行的.这对于确定合理的冲压工艺方案和模具结构设计具有重要的实用价值.
展开▼