Stress Corrosion Cracking and Electrochemical Potential of Titanium Alloys

摘要

This paper considers the relationship of electrochemical parameters and corrosion resistance stress cracking (SCC - Stress corrosion cracking) of titanium alloys in artificial seawater. It is established that there is a correlation between the decrease of the resistance SCC low-cycle fracture and the change of the potential of oxygen evolution.