Influence of Melting Conditions on Graphite Morphology in Spheroidal Graphite Cast Iron Using Ni-C Alloys

摘要

The effects of the cooling rate, atmosphere and holding time on the graphite morphology of spheroidal graphite cast iron were studied using Ni-C alloys. Two groups of parent alloys were prepared using high purity materials, i.e., Group 1 containing the spheroidizing element of Ce, Mg or Ca, while in Group 2, S was added as an anti-spheroidizing element. For discussing the influence of the cooling rate on the graphite morphology, 0,5g of the Group 1 samples were melted and held for 15 minutes at 1673K in an Ar atmosphere, then cooled at 1000K/min or 20K/min. The results showed that perfect spheroidal graphite could not be confirmed, while irregular graphite appeared.