Electrochemical corrosion behavior of arc sprayed Zn-Al coatings

摘要

Cored wires and high velocity arc spraying (HVAS) technique were applied to produce high Al content Zn-Al alloy coatings on low carbon steel substrates. The electrochemical corrosion behaviors of Zn, Al and Zn-Al coatings were studied with potentiodynamic measurement in 5%NaCl solution. Compared with pure Zn, pure Al and Zn-15Al coatings, Zn-26Al coatings show a higher corrosion resistance in salt solution. The potentiodynamic polarization tests show that the corrosion resistance of Zn-Al coatings increases as Al content is raised. Pure Al coating exhibits different electrochemical behaviors with other coatings. The corrosion initiated at the micro-pores of the coating and the underlying corrosion mechanism is very similar to that of the pitting corrosion.