A low temperature-fired porcelain article includes a barium component in an amount of 40 to 65 wt% when calculated as BaO, a silicon component in an amount of 25 to 46 wt% when calculated as SiO2, an aluminum component in an amount of 0.1 to 20 wt% when calculated as Al2O3, a boron component in an amount of 0.3 to 1.5 wt% when calculated as B2O3, and a zinc component in an amount of 0.5 to 20 wt% when calculated as ZnO, and optionally a chromium component in an amount of 0.5 to 3.5 wt% when calculated as Cr2O3. The porcelain article has a dielectric constant εr of not more than 10, a quality coefficient Q of not less than 2500, and an absolute value of a temperature coefficient τf of the resonance frequency of not more than 30 ppm/°C, and is suitable for use in electronic components.
展开▼
机译:低温烧制的陶瓷制品包括以BaO计为40至65重量%的钡成分,以SiO 2 Sub>计为25至46重量%的硅成分,当以Al 2 Sub> O 3 Sub>计算时,铝组分的含量为0.1至20 wt%;当以B计算时,硼组分的含量为0.3至1.5 wt% 2 Sub> O 3 Sub>,锌成分的含量为0.5至20 wt%(按ZnO计算),铬成分的含量为0.5至3.5 wt%当计算为Cr 2 Sub> O 3 Sub>时。该瓷器的介电常数εr为10以下,品质系数Q为2500以上,共振频率的温度系数τf的绝对值为30ppm /℃以下,是合适的。用于电子元件。
展开▼