Polytrimethylene terephthalate fiber, cheese-shaped bobbin, process to produce a polytrimethylene terephthalate fiber, preliminary twist textured yarn, bobbin, process to produce a preliminary twist textured yarn, and, fabric
Polytrimethylene terephthalate fiber, cheese-shaped bobbin, process to produce a polytrimethylene terephthalate fiber, preliminary twist textured yarn, bobbin, process to produce a preliminary twist textured yarn, and, fabric
"POLYTHRIMETHYLENE TEREFTALATE FIBER, CHEESE SHAPE SPULA, PROCESS TO PRODUCE A POLYTHRIMETHYLENE TEREPTALATE FIBER, PRELIMINARY TORRING TEXTURED YARN, SPRAY YARN, PROCESS TO PRODUCE A TEXTURED, TEXTURED YARN". A polytrimethylene terephthalate fiber, a process for producing it, a cheese shaped bobbin formed from it, a preliminary twist textured yarn using the fiber and a fabric using a preliminary twist textured yarn are provided. The fiber is composed of 90 moles% or more of repeat units of trimethylene terephthalate having a density in the range of 1.320 to 1.340 g / cm ^ 3 ^, a birefringence in the range of 0.030 to 0.070, a peak value of thermal stress in a range of 0.01 to 0.12 cN / dtex, a shrinkage in boiling water in a range of 3 to 40%, and an elongation at break in a range of 40 to 140%. The inventive polytrimethylene terephthalate fiber has both an appropriate crystallinity and orientation and is free of bobbin stiffness due to wire shrinkage and bulging. The inventive fiber can be produced on an industrial scale.
展开▼
机译:“聚对苯二甲酸乙二酯纤维,奶酪形状的纤维,生产聚对苯二甲酸乙二酯纤维的工艺,初步捻成色织的纱线,喷涂的纱线,生产成色的织造的纱线的过程。”提供了聚对苯二甲酸丙二醇酯纤维,其制造方法,由其形成的干酪状筒管,使用该纤维的预捻变形纱和使用预捻变形纱的织物。所述纤维由90摩尔%以上的重复单元的对苯二甲酸丙二醇酯重复单元组成,其密度在1.320至1.340g / cm ^ 3 ^的范围内,双折射在0.030至0.070的范围内,热应力的峰值在0.01〜0.12cN / dtex的范围,沸水收缩率3〜40%的范围,断裂伸长率40〜140%的范围。本发明的聚对苯二甲酸丙二醇酯纤维具有适当的结晶度和取向,并且由于线材的收缩和鼓胀而没有线轴刚度。本发明的纤维可以工业规模生产。
展开▼