SMALL-LOSS NICKEL-COPPER-ZINC FERRITE HAVING HIGH MAGNETIC FLUX DENSITY AND TRANSFORMER FOR DC-DC CONVERTER
SMALL-LOSS NICKEL-COPPER-ZINC FERRITE HAVING HIGH MAGNETIC FLUX DENSITY AND TRANSFORMER FOR DC-DC CONVERTER
展开▼
机译:DC-DC转换器具有高磁通密度和互感器的小损耗镍铜锌铁氧体
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide ferrite which can be used for a transformer of a heat-shock-resistant DC/DC converter, having large saturation magnetic flux density, being small in loss at a core.;SOLUTION: The ferrite composition comprises 46.0 to 50.5 mol% of Fe 203, 18.0 to 28.0 mol% of ZnO, more than 0 to 12.0 mol% of CuO (0 mol% is not included), and NiO for the rest as main components. An additive component of V 205 is also included by 0.1 to 0.6 wt.%.;COPYRIGHT: (C)2004,JPO
展开▼
机译:解决的问题:提供一种可用于耐热冲击DC / DC转换器的变压器的铁氧体,其饱和磁通密度大,铁芯损耗小;解决方案:该铁氧体组合物包含46.0 Fe 203为50.5摩尔%,ZnO为18.0〜28.0摩尔%,CuO为0〜12.0摩尔%以上(不包括0摩尔%),其余为NiO为主要成分。 V 205的添加成分也占0.1至0.6重量%.;版权:(C)2004,JPO