METHOD FOR THE HIGH-TEMPERATURE CATALYTIC DECOMPOSITION OF NLESS THANSBGREATER THAN2LESS THAN/SBGREATER THANO INTO NLESS THANSBGREATER THAN2LESS THAN/SBGREATER THAN AND 0LESS THANSBGREATER THAN2LESS THAN/SBGREATER THAN
METHOD FOR THE HIGH-TEMPERATURE CATALYTIC DECOMPOSITION OF NLESS THANSBGREATER THAN2LESS THAN/SBGREATER THANO INTO NLESS THANSBGREATER THAN2LESS THAN/SBGREATER THAN AND 0LESS THANSBGREATER THAN2LESS THAN/SBGREATER THAN
Method of decomposing nitrous oxide (N2O) into nitrogen and oxygen at a temperature between 700 and 1000 degreesC and at high VVH (volumetric time speeds) in the presence of a catalyst containing a mixed oxide of zirconium and cerium in the form of a solid solution The catalyst has an effective specific surface greater than 25 m2/g, preferably between 60 and 150 m2/g, and the process takes place at a VVH between 30000 and 80000 h-1. The ratio by mass of ZrO2/CeO2 in the catalyst is between 80/20 and 20/80, preferably between 70/30 and 30/70. The catalyst also contains yttrium.
展开▼
机译:在含有固溶体形式的锆和铈的混合氧化物的催化剂存在下,在700至1000摄氏度之间,高VVH(体积时速)下将一氧化二氮(N2O)分解为氮气和氧气的方法该催化剂的有效比表面积大于25m2 / g,优选为60-150m2 / g,并且该过程在30000-80000h-1的VVH下进行。催化剂中ZrO 2 / CeO 2的质量比在80/20至20/80之间,优选在70/30至30/70之间。该催化剂还包含钇。
展开▼