Production and hot forming of components of spheroidal graphite iron with elevated mechanical characteristics with an essentially bainitic structure
Production and hot forming of components of spheroidal graphite iron with elevated mechanical characteristics with an essentially bainitic structure
展开▼
机译:具有基本贝氏体组织的机械特性提高的球墨铸铁零件的生产和热成型
展开▼
页面导航
摘要
著录项
相似文献
摘要
Production and forming of components of spheroidal graphite iron with elevated mechanical characteristics consists of: preparation of a molten mixture of given composition; casting the molten mixture at 1350-1550 degrees C in a mould to obtain a draft component; extracting the draft component at a temperature (Ts) between the solidus and a temperature (AR3) representing the limit of the austenite domain; forming the draft component by hot plastic deformation to its final shape and dimensions at 1050 degrees C - Ar3 point; quenching the component to a temperature (Tb) within the bainite domain and maintaining it at this temperature for a given time (tb); and cooling the component to ambient temperature. The composition of the molten mixture (by wt %) is: (a) 3 - 4 C; (b) 1.7 - 3 Si; (c) 0.1 - 0.7 Mn; (d) 0 - 4 Ni; (e) 0 - 5 Cu; (f) 0 - 0.5 Mo; (g) a residual Mg adapted to the thickness of the components of between 0.025 and 0.80; and (h) the remainder being iron and production impurities, notably S at less than 0.015 and P at less than 0.10. An Independent claim is also included for such a spheroidal graphite iron with elevated mechanical characteristics with an essentially bainitic structure.
展开▼