Ferritic Stainless Steel Sheet Excellent in Press Formability and Secondary Formability and its Manufacturing Method

摘要

A ferritic stainless steel sheet has a composition of C up to 0.02 mass %, Si up to 0.8 mass %, Mn up to 1.5 mass %, P up to 0.050 mass %, S up to 0.01 mass %, 8.0-35.0 mass % of Cr, N up to 0.05 mass %, 0.05-0.40 mass % of Ti and 0.10-0.50 mass % of Nb with a product of (% Ti % N) less than 0.005. Precipitates of 0.15 μm or more in particle size except TiN are distributed in a steel matrix at a rate of 5000-50000/mm². The steel sheet is manufactured by hot-rolling a slab at a finish-temperature of 800° C. or lower, annealing the hot-rolled steel sheet at 450-1080° C., cold-rolling the hot-rolled steel sheet in accompaniment with intermediate-annealing at a temperature within a range of from (a recrystallization-finishing temperature −100° C.) to (a recrystallization-finishing temperature) and then finish-annealing the cold-rolled steel sheet at 1080° C. or lower. The ferritic stainless steel sheet is press-formed with high dimensional accuracy and excellent secondary formability due to controlled distribution of the precipitates.