Magnetostrictive materials, devices and methods using high magnetostriction, high strength FeGa and FeBe alloys
Magnetostrictive materials, devices and methods using high magnetostriction, high strength FeGa and FeBe alloys
展开▼
机译:使用高磁致伸缩,高强度FeGa和FeBe合金的磁致伸缩材料,装置和方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
An alloy comprising:a magnetostrictive iron alloy having the formula:FexGayAlz,where x is of from about 65 at % to about 90 at %, y is of from about 5 at % to about 35 at %, andz is of from about 0 at % to about 30 at %; andwherein said alloy has a room temperature magnetostriction of at least approximately 150 ppm.;An alloy having a saturated magnetostriction of from about at least 150 ppm comprising:a magnetostrictive iron alloy having the formula:FexGayBet,where x is of from about 65 at % to about 90 at %, y is of from about 1 at % to about 35 at %, andt is of from about 1 at % to about 30 at %; andwherein said alloy has a room temperature magnetostriction of at least approximately 150 ppm.展开▼
机译:一种合金,包括:一种具有以下通式的磁致伸缩铁合金:<?in-line-formulae description =“ In-line Formulae” end =“ lead”?> Fe x Sub> Ga y Sub> Al z Sub>, <?in-line-formulae description =“在线公式” end =“ tail”?> 其中x为约65at%至约90at%, y的范围是大约5 at%到大约35 at%,并且 ListItem> z为大约0 at%到大约30 at%;和其中所述合金的室温磁致伸缩至少约为150ppm。 ListItem> UnorderedList> ListItem> UnorderedList> ListItem> UnorderedList> ListItem> UnorderedList>;一种饱和磁致伸缩为至少约150 ppm的合金,包括:一种具有以下通式的磁致伸缩铁合金:<?in-line-formulae description =“ In-line Formulae” end =“ lead”?> Fe x Sub> Ga y Sub> Be t Sub>, <?in-line-formulae description =“在线公式” end =“ tail”?> 其中x为约65at%至约90at%, y的范围是大约1 at%到大约35 at%,并且 ListItem> t为大约1 at%至大约30 at%;和 ListItem> UnorderedList> ListItem> UnorderedList> ListItem> 其中所述合金的室温磁致伸缩至少约为150 ppm 。 ListItem> UnorderedList> ListItem> UnorderedList>
展开▼