Polystyrene-based composite resin particles, expandable composite resin particles, pre-expanded particles, and method for producing expanded molded body
Polystyrene-based composite resin particles, expandable composite resin particles, pre-expanded particles, and method for producing expanded molded body
展开▼
机译:聚苯乙烯类复合树脂颗粒,可发泡复合树脂颗粒,预发泡颗粒和制备发泡成型体的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Polystyrene-based composite resin particles comprising 100 to 500 parts by weight of a polystyrene-based resin with respect to 100 parts by weight of an ethylene-vinyl acetate copolymer resin, wherein the polystyrene-based composite resin particles are impregnated with a volatile blowing agent and are pre-expanded to obtain pre-expanded particles; the obtained pre-expanded particles are immersed in tetrahydrofuran for 24 hours to obtain an extract A; and the pre-expanded particles are divided into two halves through the center to prepare halved particles, and the halved particles are immersed in tetrahydrofuran for 24 hours to obtain an extract B; and the obtained extract A and extract B are subjected to a GPC (gel permeation chromatography) measurement and obtain the following results: the polystyrene-based resin having a weight-average molecular weight (Mw) of 100,000 to 500,000 gives a peak obtained from chromatograms for the extract A and for the extract B; and a ratio Ps : Pi stands at 1 : 10 or higher, in which Ps indicates peak top intensity of the chromatogram for the extract A, and Pi indicates peak top intensity of the chromatogram for the extract B; or a ratio Ss : Si stands at 1 : 10 or higher, in which Ss indicates a peak area of the chromatogram for the extract A, and Si indicates a peak area of the chromatogram for the extract B.
展开▼