LOW-CALCIUM SILICATE CEMENT, AND PREPARATION METHOD AND HARDENING METHOD THEREOF
LOW-CALCIUM SILICATE CEMENT, AND PREPARATION METHOD AND HARDENING METHOD THEREOF
展开▼
机译:低钙硅酸盐水泥及其制备方法和硬化方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A low-calcium silicate cement, which comprises, with the total mass of the oxides as 1, 50-60% of calcium oxide, 30-45% of silicon dioxide, 2-7% of aluminium oxide and 1-4% of iron oxide. The preparation method is as follows: crushing, grinding together and uniformly mixing raw materials to obtain a low-calcium silicate cement raw meal; calcining the raw meal at a temperature of 1050-1300°C for 30-90 min, cooling down to obtain a low-calcium silicate cement clinker, and then levigating the low-calcium silicate cement clinker to a specific surface area of 400-500 m2/kg to obtain a low-calcium silicate cement.
展开▼
机译:一种低钙硅酸盐水泥,其氧化物总量为1、50-60%的氧化钙,30-45%的二氧化硅,2-7%的氧化铝和1-4%的铁氧化物。其制备方法为:将原料粉碎,一起研磨均匀混合,得到低钙硅酸钙水泥生料。将生料在1050-1300°C的温度下煅烧30-90分钟,冷却下来以获得低钙硅酸盐水泥熟料,然后将低钙硅酸盐水泥熟料悬浮至比表面积400-500 m 2 Sup> / kg得到低钙硅酸钙水泥。
展开▼