Glossite ceramics, kiln tool using the same, and method for producing globite ceramics
Glossite ceramics, kiln tool using the same, and method for producing globite ceramics
展开▼
机译:陶粒陶瓷,使用该陶粒的窑具及其生产球状陶粒的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
In this grossite ceramics, the value of IB/IA is 0.05 or less, IB/IA being the ratio of the integrated intensity IB of the peak at 2θ=30.07º which is the main peak originating from CaAl2O4 in X-ray diffraction with respect to the integrated intensity IA of the peak at 2θ=25.47º which is the main peak originating from CaAl4O7 in X-ray diffraction, and measured under an air atmosphere, the coefficient of thermal expansion from 27ºC to 300ºC is 2.0×10-6/K or less. In a thermomechanical analysis when this grossite ceramic is heated under an air atmosphere, it is preferred that, in a size versus temperature graph obtained, either a temperature region in which size decreases are observed or a plateau temperature region in which size does not substantially change is observed.