FIELD: construction.;SUBSTANCE: invention relates to the industry of construction materials and can be used in making articles in civil and industrial construction, monolithic construction, when erecting special-purpose structures. Nanomodified high strength lightweight concrete has an average density of 1,300…1,510 kg/m3; compression strength limit 50.5…65.8 MPa; specific strength 38.8…43.6 MPa; coefficient of crack resistance 0.084…0.085; modulus of elasticity 6.10…8.22 GPa, Poisson ratio 0.093…0.136.;EFFECT: technical result is production of high-strength light concrete with high modulus of elasticity while maintaining (increasing) specific strength.;1 cl, 2 tbl
展开▼
机译:技术领域本发明涉及建筑材料工业,并且在竖立专用结构时可用于制造民用和工业建筑,整体式建筑中的制品。纳米改性高强度轻质混凝土的平均密度为1,300…1,510 kg / m 3 Sup>;压缩强度极限50.5…65.8 MPa;比强度38.8…43.6 MPa;抗裂系数0.084…0.085;弹性模量6.10…8.22 GPa,泊松比0.093…0.136 。;效果:技术成果是生产具有高弹性模量并保持(增加)比强度的高强度轻质混凝土。1cl,2 tbl