In order to improve the problem of the bad thermal storage stability of Styrene-Butadiene-Styrene Block Copolymer Modified Bitumen (SBS-modified bitumen), the vulcanization reaction was selected as the basic mechanism for the research and development of the stabilizer. Sulfur, tetramethylthiuram disulfide (TMTD), zinc oxide, butylated hydroxytoluene (BHT), kaolin (Al2O3·2SiO2·2H2O) and carbon-white (SiO2) were used as raw materials, and 32 kinds of components with different contents of raw materials were designed. The 48-h segregation softening point and other modified bitumen technical indicators, such as ductility, penetration, penetration index, viscosity, and so on, were tested and analyzed. The fluorescence microscope test was also conducted to explore the crosslinking situation based on the vulcanization reaction. The results show that the component with good performance of the SBS-modified bitumen stabilizer powder was S:TMTD:ZnO:BHT: Al2O3·2SiO2·2H2O = 60:16:4:20:1250 or S:TMTD:ZnO:BHT:SiO2 = 60:16:4:20:625. The optimum content of stabilizer powder was 0.9% (S/modified bitumen). The stabilizer was dry powder and can be directly put into bitumen. It can cross-link SBS and especially has an effect on preventing SBS segregation. The technical performance of SBS-modified bitumen with stabilizer powder, such as hot temperature performance, low temperature performance, anti-aging performance and thermal storage stability, all meet the relevant specifications.
展开▼