Natural aging and reversion behavior of Al-Cu-Li-Ag-Mg alloy Weldalite (tm) 049

摘要

This study was initiated to understand the natural aging and reversion behavior of Weldalite (trademark) 049 in tempers without cold work. Of particular interest are: (1) the microstructural basis for the high strength in the T4 condition; (2) an explanation of the reversion phenomenon; and (3) the effect of re-aging at room temperature after a reversion treatment. Mechanical properties were measured and transmission electron microscopy (TEM) analysis performed at various stages of microstructural development during aging, reversion, and subsequent re-aging.