Magnetic Fluid Friction and Wear Behavior

摘要

The friction and wear properties of two groups of magnetic fluids, one developed at NASA Lewis Research Center and a commercial fluid, were evaluated for boundary lubrication. Friction and wear measurements were made using a pin-on-disk apparatus. Three different ball materials were evaluated, (1) 440C, (2) Al2O3, and (3) Si3N4 against 440C disks. The first class of magnetic fluids have a low vapor pressure hydrocarbon base oil and are suitable for space application. Four variations of this fluid were evaluated: (1) the base oil, (2) base oil with anti-wear additives, (3) a 100 Gauss strength magnetic fluid, and (4) a 400 gauss magnetic fluid. The commercial fluid base oil and four different magnetic particle concentration levels have been evaluated. A space qualified fluorinated lubricant was tested for base line comparison. Hardness, optical microscopy, surface profilometry, and surface analysis were used to characterize the test specimens. Friction was unaffected by the concentration of magnetic particles. Wear rates for magnetic fluids were slightly higher than the base oil. The low vapor pressure magnetic fluid has better wear characteristics than the space qualified fluorinated lubricant.