Corrosion Behavior of Stainless Steels in Neutral and Acidified Sodium Chloride Solutions by Electrochemical Impedance Spectroscopy.

摘要

The objective of this work was to evaluate the corrosion performance of three alloys by Electrochemical Impedance Spectroscopy (EIS) and to compare the results with those obtained during a two-year atmospheric exposure study.' Three alloys: AL6XN (UNS N08367), 254SM0 (UNS S32154), and 304L (UNS S30403) were included in the study. 304L was included as a control. The alloys were tested in three electrolyte solutions which consisted of neutral 3.55% NaC1, 3.55% NaC1 in 0.lN HC1, and 3.55% NaC1 in 1.ON HC1. These conditions were expected to be less severe, similar, and more severe respectively than the conditions at NASA's Kennedy Space Center launch pads.