Formation of Metastable Structures and Amorphous Phases in Cu-W Alloys Using the Triod Sputtering Technique

摘要

The triode sputtering technique and a 'split-target' arrangement were used to produce metastable crystalline and amorphous phases in the Cu-W system under essentially oxygen-free conditions. Large metastable extensions of solid solubility were observed both from the Cu (fcc) and W (bcc) sides of the phase diagram, and a wide range of metallic glass formation was observed, approximately between 30 and 65 % at. W. The thickness of the amorphous Cu-W phase (40-160 mu m) that can be deposited without the formation of the metastable bcc phase appears to be dependent on the Cu-W alloy composition. On heating, the crystallization temperature of the amorphous alloys was higher than 350/degree/C. The behavior of the lattice parameter and near-neighbor distance has been studied with x-ray diffraction, showing small positive deviations from an assumed Vegard's Law. Hardness measurements indicate that the metastable crystalline phases are relatively harder than the amorphous phase. 11 refs., 9 figs. (ERA citation 13:036802)