Application of the NNWSI unsaturated test method to actinide doped SRL 165 type glass

摘要

The results of tests done using the Unsaturated Test Method are presented. These tests, done to determine the suitability of glass in a potential high-level waste repository as developed by the Nevada Nuclear Waste Storage Investigations Project, simulate conditions anticipated for the post-containment phase of the repository when only limited contact between the waste form and water is expected. The reaction of glass occurs via processes that are initiated due to glass/water vapor and glass/liquid water contact. Vapor interaction results in the initiation of an exchange process between water and the more mobile species (alkalis and boron) in the glass. The liquid reaction produces interactions similar to those seen in standard leaching tests, except due to the limited amount of water present and the presence of partially sensitized 304L stainless steel, the formation of reaction products greatly exceeds that found in MCC-1 type leach tests. The effect of sensitized stainless steel on the reaction is to enhance breakdown of the glass matrix thereby increasing the release of the transuranic elements from the glass. However, most of the Pu and Am released is entrained by either the metal components of the test or by the reaction phases, and is not released to solution. 16 refs., 20 figs., 17 tabs.