Degradation of cellulosic insulation in power transformers: A SEC-MALLS study of artificially aged transformer papers

摘要

The molecular weight distributions of artificially aged transformer papers were studied using SEC-MALLS with 0.5 % DMAc/LiCl as solvent, providing chain length distributions and averages. The slow dissolution and presence of non-cellulosic contaminants tend in some cases to introduce errors in the DP_w estimates, and a modified data processing procedure was developed to correct for extraneous scattering. Data were compared to the intrinsic viscosities obtained in 0.5 M Cuen and the 'viscosimetric DP' calculated thereof according to ISO 5351. DP_(visc) was 2-3 times lower than the weight average DP (DP_w), but closer to or slightly above the number average DP (DP_n) obtained by SEC-MALLS in the case of pure cellulose. Ageing of transformer papers were in some cases associated with changes in the polydispersity (DP_w/DP_n). The apparent degradation rate (defined as δ(1/DP)/δt) gradually decreased with time, resulting in a tendency for a 'level-off' DP in the range 200-300 for DP_(visc) and DP_n, and roughly 1,000 for DP_w.