Microstructure and dielectric properties of ferroelectric barium strontium titanate ceramics prepared by hydrothermal method

摘要

Ba{sub}xSr{sub}xTiO{sub}3, nanoparticles with different Ba compositions were synthesized by a hydrothermal method. The mechanism of hydrothermal reactions was discussed based on DTA/TG, XRD and TEM characterizations. The result showed that perovskite structure was developed through the mutual diffusion between the intermediate phases and TiO{sub}2 phase. The grain size of the Ba{sub}0.77Sr{sub}0.23TiO{sub}3 (BST77) powders was about 20-40 nm. BST ceramics were made from the hydrothermal-derived BST powders and the dielectric properties of the BST ceramics were measured. Due to the small grain size and active surface energy of the BST powders prepared by hydrothermal method, the BST ceramics showed low sintering temperature. It was found that the BST77 ceramics sintered at 1280℃ showed dielectric constant peak dispersion which was believed to be caused by dimension domino effect.