Melaminharzbasierende Duromere Wood Plastic Composites (wpc) -wärmeformbeständigkeit

摘要

This article deals with the advantages of properties - especially at higher temperatures - of WPC made of thermosets, based on a new generation of melamine resins, compared to WPC made of thermoplastics. The heat deflection temperature of WPC made of ther-moset was determined by measuring the tensile strength at higher temperatures, the creep, the thermal expansion and the heat distortion temperature (HDT) compared to WPC made of thermoplastics. The results show that it is possible to assign the special properties of thermosets - especially the heat resistance -to the wood-thermosets-composites. Additionally the differences to WPC made of thermoplastics could be pointed out. By means of annealing the heat deflection temperature of WPC made of thermosets could be improved.%Dieser Artikel behandelt die Eigenschaftsvorteile - insbesondere bei höheren Temperaturen -von vernetzten duromeren WPC basierend auf einer neuen Generation von extrudierbaren Melaminharzen im Vergleich zu WPC aus Thermoplasten. Zur Bestimmung der Wärmeformbeständigkeit wurden von diesen duromeren WPC die Zugfestigkeit bei höheren Temperaturen, das Kriechverhalten, die thermische Ausdehnung und die Wärmeformbeständigkeitstemperatur (HDT - heat distortion temperature) gemessen und mit WPC aus Thermoplasten verglichen. Es zeigte sich, dass die Eigenschaft der Wärmeformbeständigkeit, welche die Duromere auszeichnet, in den Holzverbund übertragen werden konnte. Zudem wurde der Unterschied in der Wärmeformbeständigkeit zu den thermoplastischen WPC aufgezeigt. Durch eine thermische Nachbehandlung (Temperung) der duromeren WPC kann diese Eigenschaft noch weiter verbessert werden.