A Comparison of the Prediction of Fatigue Damage and Crack Growth in Adhesively Bonded Joints Using Fracture Mechanics and Damage Mechanics Progressive Damage Methods

首页> 外文期刊>The Journal of Adhesion >A Comparison of the Prediction of Fatigue Damage and Crack Growth in Adhesively Bonded Joints Using Fracture Mechanics and Damage Mechanics Progressive Damage Methods

【24h】

A Comparison of the Prediction of Fatigue Damage and Crack Growth in Adhesively Bonded Joints Using Fracture Mechanics and Damage Mechanics Progressive Damage Methods

机译：用断裂力学和渐进损伤方法对胶接接头疲劳损伤和裂纹扩展的预测比较

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

著录项
相似文献
相关主题

著录项

来源
《The Journal of Adhesion》 |2010年第12期|p.1203-1230|共28页
作者

展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类
关键词
Damage mechanics; Fatigue; Fracture mechanics; Plastic strain;

机译：损伤机理;疲劳;断裂力学;塑性应变;

相似文献

外文文献
中文文献
专利

1. A Comparison of the Prediction of Fatigue Damage and Crack Growth in Adhesively Bonded Joints Using Fracture Mechanics and Damage Mechanics Progressive Damage Methods [J] . I. A. Ashcroft, V. Shenoy, G. W. Critchlow The Journal of Adhesion . 2010,第10a12期

机译：用断裂力学和渐进损伤方法对胶接接头疲劳损伤和裂纹扩展的预测比较
2. Fracture mechanics and damage mechanics based fatigue lifetime prediction of adhesively bonded joints subjected to variable amplitude fatigue [J] . V. Shenoy, I.A. Ashcroft, G.W. Critchlow Engineering Fracture Mechanics . 2010,第7期

机译：基于断裂力学和损伤力学的变幅疲劳的胶接接头疲劳寿命预测
3. Prediction of fatigue thresholds in adhesively bonded joints using damage mechanics and fracture mechanics [J] . M. M. Abdel Wahab, I. A. Ashcroft, A. D. Crocombe Journal of Adhesion Science and Technology: The International Journal of Theoredtical and Basic Aspects of Adhesion Science and Its Applications in All Areas of Technology . 2001,第7期

机译：损伤力学和断裂力学预测粘合接头疲劳阈值的预测
4. Analysis of Creep Crack Growth in Surface Cracked Specimens:Comparisons between Approaches of Fracture Mechanics and Continuum Damage Mechanics [C] . Jian-Feng Wen, Shan-Tung Tu International conference on fracture . 2013

机译：表面裂纹试样蠕变裂纹扩展的分析：断裂力学方法与连续体损伤力学方法的比较
5. Crack Growth Rate and Crack Path in Adhesively Bonded Joints: Comparison of Creep, Fatigue and Fracture. [D] . Jhin, Minseok Greg. 2012

机译：胶接接头的裂纹扩展速率和裂纹路径：蠕变，疲劳和断裂的比较。
6. Initiation and progression of mechanical damage in the intervertebral disc under cyclic loading using continuum damage mechanics methodology: A finite element study [O] . Muhammad Qasim, Raghu N. Natarajan, Howard S. An, -1

机译：连续损伤机械方法在循环加载下椎间盘中机械损伤的启动和进展：有限元研究
7. Fracture mechanics and damage mechanics based fatigue lifetime prediction of adhesively bonded joints subjected to variable amplitude fatigue [O] . Shenoy, V, Ashcroft, IA, Critchlow, GW, 2010

机译：基于断裂力学和损伤力学的变幅疲劳的胶接接头疲劳寿命预测

A Comparison of the Prediction of Fatigue Damage and Crack Growth in Adhesively Bonded Joints Using Fracture Mechanics and Damage Mechanics Progressive Damage Methods

著录项

相似文献

相关主题

期刊订阅