Analitički model predviđanja visokocikličnog zamornog vijeka baziran na bimodalnom mehanizmu zamornog oštećenja

摘要

In this paper is considered the possibility of analytical prediction of high cycle fatigue life for cruciform welded joints, which accounts for different mechanisms of fatigue damage in crack initiation and crack propagation phase. With known material properties, numerical analysis of stress distribution and numerical simulation of fatigue crack initiation and propagation are performed. Calculated fatigue strengths show a good agreement with experimental results. Introducing the concept of crack initiation thresholdasymptotic value of Act at which initial microcrack growth rate approaches zero, this model gives the possibility to estimate fatigue limit of notched components.%U ovom raduje razmatrana mogućnost analitičkog predviđanja visokocikličnog zamornog vijeka krstastih zavarenih spojeva uz uvažavanje različitih mehanizama zamornog oštećenja u fazi inicijacije i fazi propagacije zamorne pukotine. Uz poznavanje svojstava materijala izvršena je numerička analiza raspodjele napona u strukturi i numerička simulacija inicijacije i propagacije zamorne pukotine. Dobijen je dijagram zamorne čvrstoće koji se vrlo dobro slaže sa eksperimentalnim rezultatima. Uvođenjem pojma praga opsega napona pri kome brzina rasta inicijalne mikropukotine teži nuli, ovaj model daje mogućnost procjene trajne dinamičke čvrstoće strukture sa koncentracijom napona.