Study on the Application of Kenaf Core as a Composite Reinforcement: Injection Molding of Kenaf Core/Poly(L-actide) Compounds

摘要

Injection molding was performed using poly(l-lactide) (PLLA) as a matrix and by varying the reinforcements, i.e., dry-distilled kenaf core (D-core) or untreated kenaf bast fibers, and the physical properties for these composites were subsequently compared. The dry-distillation was able to reduce the moisture content of D-core by a maximum of 4.2% as compared with untreated control core. As a result, the hydrophobicity was increased, which contributed to favorable Charpy impact strength and tensile properties of the D-core/PLLA composite relative to the kenaf bast fiber/PLLA composite. Moreover, the puffing phenomenon, which arises when heating with a microwave oven due to the vaporization of water dispersed within the interfacial regions and associated softening of the PLLA matrix by the heated vapor, was completely suppressed for the D-core/PLLA composite, whereas a large puffing ratio was observed for the kenaf bast fiber/PLLA composite. Reducing the moisture content also effectively suppressed the occurrence of transesterification reactions, leading to a decrease in the molecular weight of PLLA. However, the apparent nucleation effect of the D-core remains slightly inferior to that for the hydrophilic bast fibers due to its stronger affinity for PLLA molecules.