Intergranular stress corrosion cracking behavior of niobium-added Type 308 stainless steel weld overlay metal in a simulated BWR environment

摘要

Type 308 stainless steel weld metal as an internal cladding of reactor pressure vessels for boiling water reactors is subject to postweld heat treatment during fabrication and can suffer sensitization depending on carbon and ferrite contents. This sensitization can be avoided by using niobium-added type 308 weld metal (specified as Type 308 NbL) which was developed for one-layer overlay welding application. In the present study, stress corrosion cracking (SCC) behavior of heat-treated Types 308 and 308NbL weld metals in oxygenated high temperature pure water was evaluated by slow strain rate test and U-bend tests with and without crevice.