Polymer grafted hydroxyapatite whisker as a filler for dental composite resin with enhanced physical and mechanical properties

摘要

The objective of this study was to investigate the effect of surface graft polymerization of hydroxyapatite whisker (HW) on physical and mechanical properties of dental composite resin. Poly bisphenol A glycidyl methacrylate (Poly(Bis-GMA)) was grafted onto silanized hydroxyapatite whisker (SHW) via solution polymerization and the amount of the Poly(Bis-GMA) on the surface was effectively controlled by polymerization time. The obtained poly(Bis-GMA) grafted hydroxyapatite whisker (PGHW) with different polymer contents was filled into a resin matrix respectively, meanwhile the composites with HW and with SHW served as controls. Monomer conversion was characterized by Fourier transform infrared spectroscopy (FTIR) and volume shrinkage of the composite resin was measured with a density tester. Mechanical properties were tested with a universal testing machine. The results indicated that the composite filled with PGHW-1 h (graft ratio of poly(Bis-GMA): 8.5 wt.%) showed lower shrinkage and better mechanical properties, improving flexural strength by 6.5% and 11.9% compared with SHW filled composite and HW filled composite, respectively. However, PGHW with higher graft ratios aggregated seriously and formed defects in the composite, leading to deterioration of mechanical properties. It was revealed that the poly(Bis-GMA) on the surface of PGHW acted as a functional transition layer and enhanced interfacial compatibility and interaction between whisker and resin matrix, which facilitated the dispersion of PGHW in the composite and decreased the composite shrinkage. Thus, the graft polymerization of Bis-GMA on the surface of filler might be a promising modification method for the fabrication of dental materials.