Growth of cubic and hexagonal InN nanorods

摘要

InN nanorods with polyhedral ends were grown by evaporating indium in the flow of ammonia gas on Si substrates coated with Au catalyst. The samples were characterized by scanning electron microscopy, transmission electron microscopy (TEM), and X-ray diffraction (XRD). XRD shows that the samples contain both cubic and hexagonal phases. From the TEM results, it can be found that the cubic nanorods grow along [010] direction with a lattice constant of 0.497 nm, while the hexagonal nanorods grow along [1120] direction. The growth mechanism of the obtained nanostructures is discussed.