Template-free solvothermal synthesis of ZnO nanoparticles with controllable size and their size-dependent optical properties

摘要

ZnO nanoparticles (NPs) have been synthesized via a facile and template-free solvothermal method. The size of ZnO NPs could be tailored by adjusting the ratio of ethanol to ethylene glycol (EG). Their structure and morphology have been investigated. The as-prepared samples are monodispersed ZnO NPs with controllable sizes of about 24.2, 18.9 and 14.7 nm. The cathodoluminescence (CL) spectra of the samples show that the relative intensity ratio of the visible emission peak at 500-650 nm to the band-edge UV emission peak at 380 nm increases as the particle size decreases. Sample with smaller crystallites would have larger surface area and more oxygen vacancy defects, thus it exhibits higher visible emission peak. The UV-vis absorption spectrum indicates the band gap variation of the ZnO NPs with their size. Moreover, the size-dependent blue shifts of both the CL emission and the UV-vis absorption spectra reveal the effect of quantum confinement.