Conducting polyaniline/kaolinite composite: Synthesis, characterization and temperature sensing properties

摘要

Conductive polyaniline (PAn)/kaoIinite composite was prepared by in situ chemical polymerization by using potassium dichromate as oxidant. The changes in the conductivity and PAn content of composite with reaction conditions such as aniline/oxidant mole ratio, temperature and HCl concentration were investigated. The PAn content and conductivity of the composite reached to the maximum values of 7.3% and 24.6 × 10~(-3) S cm~(-1), respectively. The resistivity of PAn/kaolinite composite was followed during the cooling-heating cycles repeated between 5 and 120 ℃ and observed to increase with increasing temperature. The structure and the morphology of the composite were elucidated by FT1R, XRD, TGA and SEM techniques. SEM micrographs revealed that PAn was dispersed in composites as particles. The change of conductivity and microhardness values of the composite with its PAn content were also investigated.