NOWACKI'S DOUBLE SHEAR TEST IN THE FRAMEWORK OF THE ANISOTROPIC THERMO-ELASTO-VISCOPLASTIC MATERIAL MODEL

摘要

In the paper, the numerical simulation of Nowacki's double shear test in the framework of recently proposed viscoplasticity theory for anisotropic solids is presented. The numerical analysis comprises the full spatial modelling and is carried out for the DH-36 steel sheet in adiabatic conditions (the analysis of anisotropic bodies can be led only on 3D models). During analyses, strain +rates of order 10~4-10~7 s~(-1) are observed and the process time duration up to full damage (loss of continuity in the localisation zone) is around 150-300 μs. The novelty of the research is focused on the formulation that includes the anisotropy of the intrinsic microdamage process. Thus, it makes possible to obtain qualitatively and quantitatively new results compared with the existing models, like tracing the softening directions and better (closer to experiment) prediction of damage paths.%W pracy przedstawiono numeryczne symulacje testu podwójnego ?cinania, zaproponowanego przez prof. Nowackiego, w ramach sformu?owania teorii lepkoplastycz-no?ci dla anizotropowych cia? sta?ych. Analizy numeryczne obejmuj? modele trójwymiarowe i s? wykonane dla stali DH-36 w warunkach adiabatycznych (analiza cia? anizotropowych mo?e by? przeprowadzona wy??cznie na modelach trójwymiarowych). W trakcie analiz obserwuje si? pr?dko?ci deformacji rz?du 10~4-10~7 s~(-1), a czas trwania procesu do ca?kowitego zerwania próbki (utraty ci?g?o?ci w strefie lokalizacji) jest z przedzia?u 150-300μs. Oryginalno?? badań wynika z faktu uwzgl?dnienia w definicji konstytutywnego modelu anizotropowego wewn?trznego procesu mikrouszko-dzeń. W rezultacie, uzyskane wyniki daj? jako?ciowo i ilo?ciowo nowy obraz procesu, w szczególno?ci umo?liwiaj? ?ledzenie kierunków os?abienia oraz dok?adniejsze (bli?sze rezultatom eksperymentalnym) odwzorowanie ?cie?ki zniszczenia.